A scanning tunneling microscopy (STM) study of the chemistry of hydrogen on the Si(100) surface is presented. The structure and stability of the hydrogenated 2 × 1, 3 × 1 and 1 × 1 surfaces are studied. The 2 × 1 and 3 × 1 surfaces are shown to be well ordered and stable in the presence of atomic hydrogen under their respective formation conditions. In contrast, the 1 × 1 structure is poorly ordered and susceptible to spontaneous etching by hydrogen atoms. No uniform 1 × 1 dihydride phase was observed under any conditions. The existence of this intermediate 3 × 1 phase and the susceptibility of the 1 × 1 structure to etching are both shown to be due to the strain associated with the dihydride units on the 1 × 1 surface. The repulsive steric interaction between dihydride units on this surface weakens the Si-H bonds and stabilizes the 3 × 1 surface observed at 400 K. The Si-Si backbonds of these dihydride units are also strained, resulting in a lower barrier to reaction which is responsible for the etching observed on the 1 × 1 surface. © 1992.
Zelek S. Herman, Robert F. Kirchner, et al.
Inorganic Chemistry
Eloisa Bentivegna
Big Data 2022
Elizabeth A. Sholler, Frederick M. Meyer, et al.
SPIE AeroSense 1997
Xikun Hu, Wenlin Liu, et al.
IEEE J-STARS