Electrooptic single crystals having a room temperature tetragonal tungsten bronze-type structure were grown from the pseudosystem KNbO3LiNbO3BaNb2O6 using covered platinum crucibles cooled at 2°C/hr. The largest and best quality crystals were grown from molten solutions with compositions approximately between K3Li2Nb5O15 and KBa2Nb5O15. The K3Li2Nb5O15 functions as a flux and the compositions of the grown crystals lie close to KBa2Nb5O15. These tungsten bronze-type crystals, which can be represented as KBa2Nb5O15 solid solutions with LiNbO3 and K3Li2Nb5O15, are not microtwinned and a large range of the bronze compositions phase match the Nd laser (1.06 μ) for second harmonic (0.53 μ) generation without double refraction above room temperature. © 1970.
Kigook Song, Robert D. Miller, et al.
Macromolecules
T.N. Morgan
Semiconductor Science and Technology
I.K. Pour, D.J. Krajnovich, et al.
SPIE Optical Materials for High Average Power Lasers 1992
J.K. Gimzewski, T.A. Jung, et al.
Surface Science